Location: Home > Product > Ceramic Composite Casting(MMC castings) > MMC liner- Ceramic insert liner

MMC chute liner ceramic insert chute liner MMC liner
  • MMC liner- Ceramic insert liner




MMC liner for Ball mill, Vertical mill (VRM), AG/SAG, Crusher Liner, Chute Liner, storage bin.

Detail:

高铬陶瓷复合铸造立磨(钢渣磨、水泥磨、磨煤机)辊套、碾底衬板,导向板等产品具有超高耐磨性能,平均磨损深度为每1000小时1-3mm;使用寿命是常规高铬产品的2倍以上。

陶瓷复合铸造衬板(MMC-衬板),广泛应用于球磨机、立式磨机(VRM)、自磨机/半自磨机、破碎机、溜槽、储料仓等设备耐磨部位。高铬陶瓷复合铸造衬板(MMC-Cr-衬板)具有高硬度,高耐磨性高铬复合铸造辊套及衬板的平均磨损深度为每1000小时2-3mm(高铬衬板每1000小时10-15mm);高耐磨性高铬复合铸造导向板的平均磨损深度为每1000小时小于1mm;高耐磨性高铬复合铸造溜槽衬板的平均磨损深度为每1000小时10mm(高铬衬板每1000小时25-30mm)。

马氏体钢基陶瓷复合铸造衬板(MMC-M-衬板),MMC-M-衬板可焊接加工..耐磨板具有很好的焊接性能,同时承受较高的冲击.

MMC liner for Ball mill, Vertical mill (VRM), AG/SAG, Crusher, Chute, storage bin.

1, High Cr cast iron matrix ceramic composite casting liner ( MMC-Cr-Liner) ,
the MMC-Cr liner has high hardness, high wear resistance
The average wear depth of the high-chromium composite casting roll sleeve and liner is 2-3mm per 1000 hours
(high-chromium roller and liner is 10-15mm per 1000 hours)
The average wear depth of the high-chromium composite casting Chute liner is 10mm per 1000 hours
(high-chromium Chute liner is 25-30mm per 1000 hours)

2, Martensite steel matrix ceramic composite casting liner ( MMC-M-Liner) ,
The MMC-M liner can be welded and machining.
The wear-resistant  plate has very good welding performance while bearing high impact.

Use Example of Ceramic insert liner of ZGM95 Vertical mill (max lose 23-26mm after 8700hour)
Material= Coal HGI=60
Feed size= 30-50mm
The average wear depth of the high-chromium composite casting roll sleeve and liner is 2-3mm per 1000 hours
(high-chromium roller and liner is 10-15mm per 1000 hours)

Hits:  UpdateTime:2020-05-19 13:19:08  【Printing】  【Close
Pre Item:None
Next Item:ceramic inlay blow bar
  • BEIJING JINMEI ENTREPRENEUR CO .,LTD
  • Tel: 86-10-8890 9291/8890 9293 Fax: 86-10-8890 9288 Email: info@djm-bj.com
  • Room No.1403 TaiRan Building, No.36 GuSheng Road, ShiJingShan District, Beijing, China.100043
  • Copyright 2006-2018 DJM All Right Reservered. Report To Improve Product
    京ICP备11022145号-2 & 京公网安备110107000026
  • MMC Mill part, MMC Impact bar, MMC Mantle, MMC Crusher part, Ceramic composite High Mn Steel, ceramic particules composite casting,ceramic Insert composite castings
Powered by  MetInfo  3.0 ©2008-2020  www.MetInfo.cn